HW811 Agglomerated, Fluoride-basic Flux（basicity：1.4）
◆ AWS A5.17 F7A2-EM12K F7A4-EH14
◆ Grain size: 10-40mesh
◆ Density:1.3g/cm3
Retail price
0.0
元
Market price
0.0
元
Number of views:
1000
Product serial number
Quantity
-
+
Stock:
0
Product description
Parameters
◆ GB/T 12470 F48A2-H08MnA F48A4-H10Mn2
◆ AWS A5.17 F7A2-EM12K F7A4-EH14
◆ Grain size: 10-40mesh
◆ Density:1.3g/cm3
|
Flux/ wire combination |
Rm （Mpa） |
ReL / Rp0.2 （Mpa） |
A （%） |
V type Groove impact |
|
| -20℃(J) | -40℃(J) | ||||
|
H08MnA |
500 | 390 | 32 | 120 | / |
|
H10Mn2A |
530 | 420 | 29 | / | 80 |
|
H08MnMoA |
575 | 480 | 25 | 85 | / |
◆ Application
◆ It can be used for multilayer, double sided single pass welding
◆ With H08A, H08MnA and H10Mn2, it is suitable for welding of light and heavy steel structure.
◆ Applied with 90 degree angle, the deposited metal has good slag removal，has smooth welding bead
◆ Suitable for steel structure: light steel( H beam), heavy steel(H beam、box column)
◆ With H08A, 50-6, It can be used for welding of big and small diameter spiral and straight seam pipes of class L210-L415.
◆ In high current condition, with a welding speed of 1.8m/min, it has better anti porosity ability, and the slag removal is long strip state and easy to take off. Good weld finish.
◆ Recommended industry: 40 kg class spiral pipe, straight seam pipe and below.
◆ With H10Mn2, it can be applied on the boiler, air tower. and with H08A, it can be used to repair the carbon steel roller，
◆ It conforms to NB/T 47018-2011 (technical specification for welding material ordering of pressure equipment requirements).
◆ Recommended industry: 40 kg and below the spiral pipe, wind tower, vessel deck welding.
|
H Beam Steel Structure |
Heavy Steel Structure (Box Column) |
 |
 |
Next
None
Recommended Products
-
HW931 Agglomerated, Calcium-Silicate Flux (basicity: 1.0)◆ Confrom to: GB/T5293 F4A0-H08A、 F5A2-H08MnA AWS A5.17 F7A2-EM12K ◆ Description ◆ Grain Size: 10-60mesh ◆ Density: 1.25g/cm3HW931 Agglomerated, Calcium-Silicate Flux (basicity: 1.0)0.00◆ Confrom to: GB/T5293 F4A0-H08A、 F5A2-H08MnA AWS A5.17 F7A2-EM12K ◆ Description ◆ Grain Size: 10-60mesh ◆ Density: 1.25g/cm3 -
HW811Q Agglomerated,Fluoride Basic flux(Basicity: 2.4)◆ GB/T12470 F48A4-H10Mn2 F55A4-H08MnMoA ◆ AWS A5.17 F7A2-EH14 ◆ NB/T47018-2011 ◆ Grain size：10-40mesh ◆ Density：1.45g/cm3HW811Q Agglomerated,Fluoride Basic flux(Basicity: 2.4)0.00◆ GB/T12470 F48A4-H10Mn2 F55A4-H08MnMoA ◆ AWS A5.17 F7A2-EH14 ◆ NB/T47018-2011 ◆ Grain size：10-40mesh ◆ Density：1.45g/cm3 -
GX-B agglomerated flux (Basicity: 1.5)◆ Conforms to:GB/T 12470 F48A4-H08MnA F55A4-H08 AWS A5.23M F48A4-EM12K F55A4-EG-G ◆ General information: ◆ Basicity：1.6 ◆ density：1.2g/cm3 ◆ Grain size：10-40mesh ◆ Polarity：DCEPGX-B agglomerated flux (Basicity: 1.5)0.00◆ Conforms to:GB/T 12470 F48A4-H08MnA F55A4-H08 AWS A5.23M F48A4-EM12K F55A4-EG-G ◆ General information: ◆ Basicity：1.6 ◆ density：1.2g/cm3 ◆ Grain size：10-40mesh ◆ Polarity：DCEP -
HW833 agglomerated, Calcium-Silicate flux (Basicity: 0.8)◆ AWS A5.17 F6A0-EL12 F7A2-EM12K ◆ Grain Size: 10-40 mesh ◆ Density: 1.2g/cm3 ◆ Polarity: DCEP/ACHW833 agglomerated, Calcium-Silicate flux (Basicity: 0.8)0.00◆ AWS A5.17 F6A0-EL12 F7A2-EM12K ◆ Grain Size: 10-40 mesh ◆ Density: 1.2g/cm3 ◆ Polarity: DCEP/AC -
HW811G Agglomerated,Fluoride Basic Flux （Basicity：1.6）◆ GB/T 12470 F48A4-H10Mn2 F62A4-H08MnMoTiB ◆ AWS A5.17 F7A2-EM12K F7A4-EH14 ◆ NB/T47018-2011 ◆ Grain size：10-40mesh ◆ Density：1.3g/cm3 ◆ HW811G has excellent impact toughness in high heat input welding conditions. It is suitable for single wire or double wire welding ◆ HW811G is suitable for low alloy steel welding.HW811G Agglomerated,Fluoride Basic Flux （Basicity：1.6）0.00◆ GB/T 12470 F48A4-H10Mn2 F62A4-H08MnMoTiB ◆ AWS A5.17 F7A2-EM12K F7A4-EH14 ◆ NB/T47018-2011 ◆ Grain size：10-40mesh ◆ Density：1.3g/cm3 ◆ HW811G has excellent impact toughness in high heat input welding conditions. It is suitable for single wire or double wire welding ◆ HW811G is suitable for low alloy steel welding. -
HW811A Agglomerated,Aluminate Basic Flux（ Basicity：1.1 ）◆ GB/T 12470 F48A4-H10Mn2 F55A4-H08MnMoA ◆ AWS A5.17 F7A4-EM12K-H8 F8A4-EA2 ◆ Grain size:10-40 mesh ◆ Density: 1.4g/cm3HW811A Agglomerated,Aluminate Basic Flux（ Basicity：1.1 ）0.00◆ GB/T 12470 F48A4-H10Mn2 F55A4-H08MnMoA ◆ AWS A5.17 F7A4-EM12K-H8 F8A4-EA2 ◆ Grain size:10-40 mesh ◆ Density: 1.4g/cm3 -
HW811T Agglomerated Fluoride-Basic Low Hydrogen Flux（Basicity: 2.8）◆ GB/T 12470 F48A4-H10Mn2 F62A4-H08CH4 ◆ AWS A5.23 F7A4-EM12K F9A4-EG-G ◆ Grain size：10-40mesh ◆ Density：1.4g/cm3HW811T Agglomerated Fluoride-Basic Low Hydrogen Flux（Basicity: 2.8）0.00◆ GB/T 12470 F48A4-H10Mn2 F62A4-H08CH4 ◆ AWS A5.23 F7A4-EM12K F9A4-EG-G ◆ Grain size：10-40mesh ◆ Density：1.4g/cm3 -
HW811I Agglomerated,Aluminate Basic Flux （Basicity: 1.4 ）◆ GB/T 5293 F4A0-H08MnA F5A2-H10Mn2 ◆ Grain size: 10-40 mesh ◆ Density：1.25g/cm3HW811I Agglomerated,Aluminate Basic Flux （Basicity: 1.4 ）0.00◆ GB/T 5293 F4A0-H08MnA F5A2-H10Mn2 ◆ Grain size: 10-40 mesh ◆ Density：1.25g/cm3 -
HW821T Agglomerated,Fluoride-Basic Low Hydrogen Flux（Basicity: 3.1）◆ GB/T 12470 F48A4-H10Mn2H5 ◆ AWS A5.23M F7A4-EM12K ◆ Grain size：10-40mesh ◆ Density: 1.25g/cm3HW821T Agglomerated,Fluoride-Basic Low Hydrogen Flux（Basicity: 3.1）0.00◆ GB/T 12470 F48A4-H10Mn2H5 ◆ AWS A5.23M F7A4-EM12K ◆ Grain size：10-40mesh ◆ Density: 1.25g/cm3
-
HW60D Agglomerated stainless steel Flux (welding strip)(Basicity : 2.2)◆ Conforms to: GB/T 17854 F308L-H00Cr21Ni10/ F309L-H00Cr24Ni13/ F316L-H00Cr19Ni12Mo2 ◆ General information ◆ Fluoride-basic type agglomerated flux ◆ Density：1.3g/cm3 ◆ Grain size：10-40mesh ◆ ApplicationHW60D Agglomerated stainless steel Flux (welding strip)(Basicity : 2.2)0.00◆ Conforms to: GB/T 17854 F308L-H00Cr21Ni10/ F309L-H00Cr24Ni13/ F316L-H00Cr19Ni12Mo2 ◆ General information ◆ Fluoride-basic type agglomerated flux ◆ Density：1.3g/cm3 ◆ Grain size：10-40mesh ◆ Application
-
HW861 Agglomerated Stainless Steel Flux (basicity: 1.8)◆ Conforms to: GB/T 17854 F308L-H00Cr21Ni10 F309- H0Cr24Ni13 F316L-H00Cr19Ni12Mo2 ◆ General information ◆ Density：1.2-1.25g/cm3 ◆ Grain size：10-40mesh ◆ Polarity：DPEC ◆ ApplicationHW861 Agglomerated Stainless Steel Flux (basicity: 1.8)0.00◆ Conforms to: GB/T 17854 F308L-H00Cr21Ni10 F309- H0Cr24Ni13 F316L-H00Cr19Ni12Mo2 ◆ General information ◆ Density：1.2-1.25g/cm3 ◆ Grain size：10-40mesh ◆ Polarity：DPEC ◆ Application
-
HW751H Agglomerated, Zirconium-Silicate flux (Basicity: 0.8)◆ AWS A5.17 F7A0-EL12 F7A0-EM12K ◆ Grain Size: 16-80 mesh ◆ Density: 1.5g/cm3 ◆ Polarity: DCEP/AC ◆ fine particle welding ◆ High speed weldingHW751H Agglomerated, Zirconium-Silicate flux (Basicity: 0.8)0.00◆ AWS A5.17 F7A0-EL12 F7A0-EM12K ◆ Grain Size: 16-80 mesh ◆ Density: 1.5g/cm3 ◆ Polarity: DCEP/AC ◆ fine particle welding ◆ High speed welding -
HW751T Agglomerated, Aluminate Rutile flux (Basicity: 0.7)◆ AWS A5.17 F7A0-EM13K F7A0-EL12-H8 F7A2-EM12K ◆ Grain Size: 10-40 mesh ◆ Density: 1.4g/cm3 ◆ Polarity: DCEP/ACHW751T Agglomerated, Aluminate Rutile flux (Basicity: 0.7)0.00◆ AWS A5.17 F7A0-EM13K F7A0-EL12-H8 F7A2-EM12K ◆ Grain Size: 10-40 mesh ◆ Density: 1.4g/cm3 ◆ Polarity: DCEP/AC -
HW751L agglomerated, Aluminate Rutile flux (Basicity: 0.7)◆ AWS A5.17 F7A0-EL8 F7A0-EM12K ◆ Grain size: 12-60 mesh ◆ Density: 1.4g/cm3 ◆ Polarity: DCEP/ACHW751L agglomerated, Aluminate Rutile flux (Basicity: 0.7)0.00◆ AWS A5.17 F7A0-EL8 F7A0-EM12K ◆ Grain size: 12-60 mesh ◆ Density: 1.4g/cm3 ◆ Polarity: DCEP/AC -
HW751A（Aluminum-base flux Basicity: 1.1 Similar to Lincoln 960◆ AWS A5.17 F7A2-EM13K-H8 F7A2-EM12K-H8 F7A4-EM14K-H8 ◆ Grain Size: 10-40 mesh ◆ Density: 1.4g/cm3 ◆ Polarity: DCEP/ACHW751A（Aluminum-base flux Basicity: 1.1 Similar to Lincoln 9600.00◆ AWS A5.17 F7A2-EM13K-H8 F7A2-EM12K-H8 F7A4-EM14K-H8 ◆ Grain Size: 10-40 mesh ◆ Density: 1.4g/cm3 ◆ Polarity: DCEP/AC -
HW751 Agglomerated, Aluminate Rutile Flux (Basicity: 0.7)◆ GB/T 5293 F5A0-H08A F5A2-H08MnA ◆ AWS A5.17 F6A0-EL8 F7A2-EM12K ◆ Grain Size: 10-60 mesh ◆ Density: 1.4g/cm3 ◆ Polarity: DCEP/ACHW751 Agglomerated, Aluminate Rutile Flux (Basicity: 0.7)0.00◆ GB/T 5293 F5A0-H08A F5A2-H08MnA ◆ AWS A5.17 F6A0-EL8 F7A2-EM12K ◆ Grain Size: 10-60 mesh ◆ Density: 1.4g/cm3 ◆ Polarity: DCEP/AC -
HW930 Agglomerated,Calcium-Silicate Flux (basicity: 0.7)◆ GB/T5293 F4A0-H08A 、 F4A0-H08MnA ◆ AWS A5.17 F5AZ-EM12K ◆ Grain size：10-40mesh ◆ Density: 1.1g/cm3HW930 Agglomerated,Calcium-Silicate Flux (basicity: 0.7)0.00◆ GB/T5293 F4A0-H08A 、 F4A0-H08MnA ◆ AWS A5.17 F5AZ-EM12K ◆ Grain size：10-40mesh ◆ Density: 1.1g/cm3 -
HW931G Agglomerated, Calcium-Silicate Flux (basicity: 0.9)◆ GB/T5293 F5A0-H08MnA F5A2-H10Mn2 ◆ Grain size：10-40mesh ◆ Density: 1.20g/cm3HW931G Agglomerated, Calcium-Silicate Flux (basicity: 0.9)0.00◆ GB/T5293 F5A0-H08MnA F5A2-H10Mn2 ◆ Grain size：10-40mesh ◆ Density: 1.20g/cm3 -
HW812D Agglomerated,Mill Roller Hardfacing flux（Basicity：2.4）◆ GB/T 17854 F410-H1Cr13 F430-H1Cr17 ◆ Grain size：10-40mesh ◆ Density: 1.35g/cm3HW812D Agglomerated,Mill Roller Hardfacing flux（Basicity：2.4）0.00◆ GB/T 17854 F410-H1Cr13 F430-H1Cr17 ◆ Grain size：10-40mesh ◆ Density: 1.35g/cm3
-
HW811NQ Agglomerated,Fluoride Basic Flux（Basicity：1.8）◆ GB/T12470 F48A4-H10Mn2 ◆ TB/T 2374-2008 TH550-NQ-Ⅲ ◆ NB/T47018-2011 ◆ Grain size：10-40mesh ◆ Density：1.3g/cm3HW811NQ Agglomerated,Fluoride Basic Flux（Basicity：1.8）0.00◆ GB/T12470 F48A4-H10Mn2 ◆ TB/T 2374-2008 TH550-NQ-Ⅲ ◆ NB/T47018-2011 ◆ Grain size：10-40mesh ◆ Density：1.3g/cm3
Copyright © Zhengzhou Feng Huang New Material Technology Co., Ltd.
Leave a message
客户留言
Description:
Zhengzhou Feng Huang New Material Technology Co., Ltd.
Headquarters: 27th Floor, Greenland Century Summit, No. 12, Business Outer Ring, Zhengdong New District, Zhengzhou City, Henan Province
Factory: Xiaoguan Duanhe Industrial Park, Gongyi, Zhengzhou City, Henan Province
Cell phone：+86-13526605782 （Manager Xu）
E-mail：phx04@fenghuanghj.com
Copyright © Zhengzhou Feng Huang New Material Technology Co., Ltd. 豫ICP备14018313号-1 Powered by www.300.cn