H10Mn2

Category:

Submerged Arc Welding Wire

Carbon steel high-manganese submerged-arc welding wire exhibits excellent low-temperature toughness and strength. When used with different fluxes, it is suitable for welding various low-alloy steels; in combination with SJ101/HJ431, it is ideal for welding Q345 medium- and thick-gauge plates, while when paired with SJ101G, it is well-suited for X65-grade pipeline steel applications.

Keywords:

H10Mn2

Online Consultation

Product Description

Quite standard

Compliant

GB/T 12470 F48A4-H10Mn2

Equivalent to

AWS A5.23 F7A4-EH14

Characteristics and Applications

Single-wire multi-pass and multi-wire single-pass welding are both feasible.

Precautions

Thoroughly remove rust, moisture, oil, and dust from the welding area.

Maintain the integrity of the TIP;

Perform welding using this welding wire within the optimal welding condition range whenever possible.

An example of the chemical composition of welding wire ( wt % )
C	Mn	Yes	P	S
0.070	1.72	0.03	0.012	0.010

Typical Mechanical Property Values of Deposited Metal
Tensile strength ( megapascal )	Yield strength ( megapascal )	Elongation ( % )	AVK Impact energy -40 °C)
580	485	28	110

Welding Parameter Recommendations ( DC+ )
Wire diameter mm	Current range A	Voltage range V	Welding speed ± 0.5mm/s	Dry extension length mm
2.0	300-400	26-29	5.5	13-19
2.4	350-450	27-30	6.0	19-32
2.8	400-500	27-30	6.0	19-32
3.0	400-500	27-30	6.5	25-38
3.2	425-525	27-30	6.5	25-38
4.0	475-575	27-31	7.0	25-38
5.0	550-650	27-31	7.0	25-38
6.4	700-800	28-32	8.5	38-50

Package dimensions
Wire diameter ( mm)	2.0, 2.5, 3.0, 3.2, 4.0, 4.5, 4.8, 5.0, 6.4
Weight ( kilogram )	25, 50, 150, 350, 1000
Remarks	The above can be customized according to customer requirements.